PP
Item
Test Standard
Unit
Typical Performance
P1000
P1304
P201
P401
P302
P304
P306
P3010
P830
P840
P860
P353
Density
D792
g/cm3
1.15
1.28
0.90
0.90
1.02
1.08
1.14
1.34
1.00
1.04
1.14
1.42
Tensile Strength
D638
MPa
20
30
15
20
30
60
80
90
20
25
30
120
Elongation at Break
D638
%
2
2
100
10
2
2
2
2
3
3
3
2
Bending Strength
D790
MPa
30
60
20
25
50
80
100
120
30
35
45
190
Flexural Modulus
D790
MPa
1200
2800
800
1000
2500
3500
4500
6000
1200
1500
2000
7500
Notched Impact Strength of Cantilever
D256
kJ/㎡
5.0
5.0
40.0
15.0
6.0
7.0
7.0
6.0
5.0
6.0
6.0
5.0
Rockwell Hardness, HRR
D785
——
90
100
60
70
110
110
115
118
90
100
105
120
Melting Point
 
170
175
170
170
175
175
175
175
170
170
170
175
Heat Distortion Temperature, 0.45MPa
D648
90
140
85
90
120
130
145
150
100
110
120
140
Flame Retardance
UL94
Grade
V0
V0
HB
HB
HB
HB
HB
HB
HB
HB
HB
HB
Surface Resistance
D257
Ω
1015
1016
1016
1016
1016
1016
1016
1016
1014
1014
1014
1015
Dielectric Strength
D149
KV/mm
19
19
15
15
15
15
15
15
19
19
19
16
Mould Shrinkage
D955
mm/mm
0.01
0.004
0.02
0.018
0.008
0.005
0.003
0.002
0.016
0.015
0.01
0.001
Filling Amount
 
%
——
GF20
——
——
GF10
GF10
GF30
GF50
M15
M20
M30
GF15+M25
Features
General flame retardant type
Glass fiber reinforced flame retardant type
Toughening high impact type
Glass fiber reinforced type
Mineral reinforced type
Glass fiber mineral reinforced type
Use
Electronic component
Electronics connector
Automotive radiator
Textile equipment, engine blower, auto parts, electronic components
Auto parts, electronics, mechanical parts
Mechanical parts